Article No. 689411
Very fast reacting, pigmented synthetic resin coating
Product specifications
The stated values represent typical product characteristics and are not to be construed as binding product specifications.
Field of application
- Coloured coating for roller application
- Base layer for blinded covers
- Base layer for flake coatings
- Top sealant for blinded covers
- Marking paint
Properties
- Full hardening from +3 °C
- Resistant to wear
- Can be subjected to mechanical loads
- Can be subjected to chemical loads
-
Preparation
-
Substrate requirements
The substrate must be firm, dimensionally stable, capable of bearing loads and free of loose constituents, dust, oil, grease, rubber marks and other substances that could interfere with adhesion.
The tensile strength of the surface of the substrate must be at least 1.5 N/mm² on average (smallest individual value of at least 1.0 N/mm²), and the compressive strength must be at least 25 N/mm².
The following Remmers primers must be used: QP Primer, Epoxy MT 100, Epoxy ST 100, Epoxy FAS 100.
The primer must be pore-filling in order to act as protection against alkalis.
See the current Technical Data Sheet of the product in question and the system recommendations for more detailed information.
-
-
Preparation
-
Combination container
Add the entire quantity of the hardener (component B) to the base compound (component A).
Then add the entire quantity of component C.
Mix thoroughly with a slow-speed electric mixer
(approx. 300 - 400 rpm).Mix for at least 3 minutes.
Insufficient mixing is indicated by streaks forming.
-
Application
-
The times given are reduced at higher temperatures and increased at lower temperatures, in particular in combination with high humidity.
The material can be accelerated by the extra addition of QP CAT
(see Technical Data Sheet).
This is recommended in particular for substrate temperatures < +12 °C.
-
Working tools / cleaning
-
Rubber scraper, epoxy roller, suitable mixing apparatus
-
More detailed information can be found in the Remmers Tool Programme.
Clean tools, equipment and splashed material immediately while fresh with V 101.
Take suitable protective and waste disposal measures when cleaning.
-
Storage / shelf life
-
If stored unopened in its original container in a cool, dry place and protected against frost, the product will keep for at least 12 months.
-
Usage
-
Dependent on application (see Technical Data Sheet)
-
-
Application examples
-
Base layer for blinded coatings
Pour the material onto the prepared surface and spread using a suitable epoxy roller.
Scatter an excess of quartz sand or Colorid/sediment flakes over the base layer while it is still wet.
Remove any loose, excess material after hardening.
Then, apply the fixing agent or sealant as per the system specifications.
Approx. 0.3-0.4 kg/m² binder
-
Top sealant
Remove any loose, excess material after hardening.
Pour the material onto the prepared surface, spread evenly using a rubber scraper, then roll crossways using a suitable epoxy roller.
0.6 - 0.8 kg/m² binder (depending on the blinding material)
-
Roller coating
Pour the material onto the prepared surface and spread using a suitable epoxy roller.
The application rate depends on the substrate, temperature, required coating thickness, and optical requirements.
approx. 0.3 kg/m² binder
-
-
General information
-
Unless otherwise specified, all of the values and application rates given above have been determined under laboratory conditions (20 °C) using standard colours. Slight deviations from these values may arise if the product is worked with on site.
The QP material must be applied to the Remmers EP/QP coating within 24 hours.
When using for marking work, the adhesive tape must be removed while the material is still wet.
Use sufficiently experienced personnel to ensure that surfaces are as even as possible.
Uneven application, strong draughts and large temperature differences on the surface can result in a non-uniform surface appearance due to differences in the degree of gloss.
Abrasive mechanical loads leave traces of wear.
Weathering and use may cause changes in the colour and surface.
On account of the reaction heat that is generated in accelerated systems, the applicable coating thicknesses must be observed.
As a general rule, the binder is not saponification stable.
Not suitable for permanently wet areas.
Excessive leftover quantities of material in the container will result in the development of smoke and odours if the pot life is exceeded.
Further notes on working, system construction and maintenance of the listed products can be found in the latest Technical Data Sheets and the Remmers system recommendations.
-
-
Disposal instructions
-
Larger quantities of leftover product should be disposed of in the original containers in accordance with the applicable regulations. Completely empty, clean containers should be recycled. Do not dispose of together with household waste. Do not allow to enter the sewage system. Do not empty into drains.
-
-
Safety / regulations
-
Restricted to professional users.
Further information concerning safety during transport, storage and handling as well as on disposal and ecology can be found in the latest Safety Data Sheet.
-