    Article No. 639411

    Epoxy BS 3000 AS

    Dissipative, pigmented sealant

    Colour: special colours from 100 kg | 6394
    Size / Quantity

    Product specifications

    On delivery

    Resistance to ground < 10^6 Ω (system resistance)
    Solids content 65% by mass

    Component A

    Density (20°C) 1.4 g/cm³
    Viscosity (25 °C) 400 mPa s

    Component B

    Density (20°C) 1.1 g/cm³
    Viscosity (25 °C) 200 mPa s

    Mixture

    Density (20°C) 1.5 g/cm³
    Viscosity (25 °C) 750 mPa s

    The stated values represent typical product characteristics and are not to be construed as binding product specifications.

    Field of application

    • Sealant in conductive systems

    Properties

    • Water-based
    • Water vapour diffusion capable
    • Silk gloss
    • Conductive
    • Physiologically harmless once fully cured
    • Preparation
      • Substrate requirements

        The substrate must be firm, dimensionally stable, capable of bearing loads and free of loose constituents, dust, oil, grease, rubber marks and other substances that could interfere with adhesion.

        The tensile strength of the surface of the substrate must be at least 1.5 N/mm² on average (smallest individual value of at least 1.0 N/mm²), and the compressive strength must be at least 25 N/mm².

        A suitable Remmers epoxy primer or epoxy scratch coat must always be used.

      • Preparations

        Before the application of the product a smooth surface must be produced, e.g. with a scratch coat.

        Refer to the current Technical Data Sheet for detailed information on the single products.

        Epoxy Conductive must be applied according to the current Technical Data Sheet as transverse conducting layer.

    • Preparation
      • Mixing ratio comp. A 80 : comp. B 20
      • Mixing time 3 min
      • Combination container

        Add the entire quantity of the hardener (component B) to the base compound (component A).

        Mix thoroughly with a slow-speed electric mixer
        (approx. 300 - 400 rpm).

        Pour the mixture into a separate container and mix again thoroughly.

        Mix for at least 3 minutes.

        Insufficient mixing is indicated by streaks forming.

    • Application
      • Application temperature: min. 8 °C max. 30 °C
      • By brush / By roller
      • Pot life 30 min
      • Application requirements

        Temperature of the material, air and substrate: from min. +8 °C to max. +30 °C.

      • The times given are reduced at higher temperatures and increased at lower temperatures, in particular in combination with high humidity.

    • Working tools / cleaning
      • By brush / By roller
      • Smoothing trowel, epoxy roller, suitable mixing apparatus

      • More detailed information can be found in the Remmers Tool Programme.

        Clean tools, equipment and any splashed material immediately with water while still fresh.

        Take suitable protective and waste disposal measures when cleaning.

    • Storage / shelf life
      • Store frost-free
      • Shelf-life 9 months
      • If stored unopened in its original container in a cool, dry place and protected against frost, the product will keep for at least 9 months.

    • Usage
      • See application examples

    • Application examples
      • Sealing

        Pour the material generously onto the surface. Use a suitable tool, e.g. a rubber scraper, to distribute the material, then roll using an epoxy roller.

        max. 0.30 kg/m² binder

    • General information
      • Unless otherwise specified, all of the values and application rates given above have been determined under laboratory conditions (20 °C). Slight deviations from these values may arise if the product is worked with on site.

        When coating continuous surfaces, only use materials with the same batch number as slight differences in colour, gloss and texture may occur.

        Due to the black transverse conducting layer, poorly covering colours are not to be used.

        Before the application of the covering layer, the correct functioning of the transverse conducting layer and of the connections must be proved and registered in a measurement report.

        Low levels of air humidity can cause a higher discharge resistance, uneven or thicker layers can even lead the coating to not be conductive at all.

        Carbon fibres are visible on the surface. Because of the way the coating is applied, the carbon fibres may bundle.

        Abrasive mechanical loads leave traces of wear.

        Epoxy resins are generally not colourfast when exposed to UV light or weather.

        In case of repairs on the surface or working up to existing surfaces, there will be a visible transition in appearance and texture.

        In order to achieve even surfaces, appropriate allowances for roughness depth must be taken into consideration.

        Suitable for vehicle traffic with rubber tyres; not suitable for vehicle loads with metal or polyamide tyres nor for dynamic point loads.

        Further notes on working, system construction and maintenance of the listed products can be found in the latest Technical Data Sheets and the Remmers system recommendations.

    • Disposal instructions
      • Larger quantities of leftover product should be disposed of in the original containers in accordance with the applicable regulations. Completely empty, clean containers should be recycled. Do not dispose of together with household waste. Do not allow to enter the sewage system. Do not empty into drains.

    • Safety / regulations
      • For professional users only!

        For further information on the safety aspects of transporting, storing and handling the product and on disposal and environmental matters, please see the current Safety Data Sheet and the brochure entitled "Epoxy Resins in the Construction Industry and the Environment", issued by Deutsche Bauchemie e.V. (2nd edition 2009).

    Possible system products